Superior functions can be brought into play under high load and low rotating speed. The solid-lubricant-inlaid bushing is based on the high intensity brass that is centrifuge cast. And then make out the loading function.
The wear plates are excellent in "friction resistance" and "self-lubrication". There is no "scoring" or "seizure" under harsh conditions.
It can still bring the superior properties into play even under high load and low rotating speed.

Part B . Product Operation

Demonstrates high performance under high-load and low-speed operations.
Apply a small amount of grease for initial lubrication in die spotting.
produced such as reciprocating motions, oscillation, frequent starts and stops, etc

Part C. Product Application

The sliding surface becomes black or black gray after operation due to the film of special solid lubricant. This is normal, do not remove film by wiping.
Demonstrates superior wear resistance in applications where oil film is seldom
Serviceable without the need for lubrication.

Types of Wear Plates
Material		Thickness	Code No.	Feautures
Base Metal	Oilless Type
FC250	Graphite	20	SESF	Excellent sliding performance at low load and medium speed.
		20	SESFT
SS400	Copper Powder sintering	20	SOX	Excellent sliding performance at low / medium load and medium speed.With the sintered layer using copper based powder and graphite, occurrence of seizure is very limited.
		20	SOXT
S45C		10	TWX
		10	TWXT
Copper alloy	Graphite	20	SESW	Excellent in load resistance and wearExcellent sliding performance at high load and low speed.resistance. Good performance is shown in reciprocating and frequent starts and stops.
		20	SESWT
		10	TWP
		10	TWPT
		5	UWP
Steel (S45C)	Graphite	20	FRP	Since the surface hardness is HRC40 or more, it is excellent in wear resistance.
Steel (SKS3)		20	TSP	Since the surface hardness is HRC58 or more, it is greatly excellent in wear resistance.